(12-21-2014, 05:40 PM)F.R.A.S It's way more expensive for NO advantages at all. So why should I like it? Second. It's a bitch welding cause it warps like crazy. Third it has a tendency to crack (ours have never done that but we use really thick tubes).
Mild steel is just cheap, easy to use and stays together for eternity
Simple as that.
(12-21-2014, 02:23 PM)Turbo why do you not like stainless steel as material FRAS?
(12-21-2014, 05:40 PM)F.R.A.S It's way more expensive for NO advantages at all. So why should I like it? Second. It's a bitch welding cause it warps like crazy. Third it has a tendency to crack (ours have never done that but we use really thick tubes).
Mild steel is just cheap, easy to use and stays together for eternity
Simple as that.